Štúdia mikroštruktúry a mechanických vlastností laserového zváraného spoja 1,5 mm Ti-6Al-4V titánovej zliatiny

Kľúčové slová:Ti-6Al-4V zliatina titánu/ laserové zváranie / mikroštruktúra / mechanické vlastnosti

Autori: Fu Heguo, Liu Guangxin, Xie Hongzhi, Jiang Wentong atď.

Shenyang Aircraft Industry Group Co., Ltd

Zdroj: zváranie a rezanie

Abstrakt: Experiment laserového zvárania plus zváranie s úpravou povrchu 1,5 mmTi-6Al-4V zliatina titánu was carried out, and the microstructure and static properties of the joint were observed. The results show that due to the influence of different welding thermal cycles, The structure area of laser welding plus surface modification welding joint can be divided into a base metal area, heat affected area, equiaxed crystal area at the bottom of weld, and columnar crystal area at the top of the weld, there is widmanstatten structure in the weld structure, With the increase of the distance from the fusion line, the microstructure of the heat-affected zone increases ' The volume fraction decreased gradually.

Mechanické vlastnosti spoja ukazujú, že pevnosť v ťahu a pevnosť v šmyku sú ekvivalentné so základným kovom a minimálny uhol ohybu je 35 stupňov, čo naznačuje, že spoj je možné použiť v strojárstve.

Morfológia zvarového spoja z titánovej zliatiny Ti-6Al-4V

Mikroštruktúra zvarovej zóny

Morfológia mikroštruktúry rôznych oblastí v tepelne ovplyvnenej zóne

Skúšobná hodnota mechanických vlastností spoja

Priemerná hodnota mechanických vlastností spoja